Partial crystallization of the erbium/ytterbium co-doped oxyfluoride glass
Erbium/Ytterbium co-doped oxyfluoride glass-ceramics can be applied as the optical fiber core. For that reason its crystallization kinetics is described in terms of the JMAK model (Johnson-Mehl-Avrami-Kolmogorov) with later updates. Differential Thermal Analysis (DTA) measurements of glass and glassceramics powders (with size comparable to the diameter of multimode optical fiber core) combined with X-ray diffraction (XRD) measurements enables both the identification of growing nanocrystals structure and determination of the specific annealing parameters. This specific glass powder annealing results in the desired microstructure of glass-ceramics fibers (nanocrystals embedded in the glassy host).
Zamiarem autorów było precyzyjne określenie warunków wygrzewania włókien optycznych ze szkieł tlenofluorkowych, współdomieszkowanych erbem i iterbem, przeznaczonych na rdzenie aktywnych światłowodów wielodomowych. Pożądana, finalna mikrostruktura włókien to jednorodnie rozłożone w matrycy szklistej nanokryształy wzbogacone w erb i iterb. Ponieważ średnica rdzeni włókien wielodomowych jest standaryzowana (50, 62,5 lub 100 μm), do badań użyto frakcji proszków szkieł o rozmiarach 45÷100 μm.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).