Anodic treatment of Zn-Ni alloy coatings in fluoride-containing alkaline solutions

Results of investigations on surface morphology (SEM), chemical composition (XPS) and corrosion resistance (LSV) of anodically oxidized Zn-Ni alloy coatings electrodeposited on steel substrate have been showed in this work. The oxidation process was carried out in the baths which are solutions of sodium hydroxide and ammonium fluoride. On the basis of the realized investigations it was found that the conversion coatings consisting of oxides and hydroxides of zinc and nickel as well as the fluorides of the metals are formed as a result of anodic treatment of the Zn-Ni coatings. The best coatings, which are characterized by the fine-crystalline passive layer without any cracks, significantly improve the corrosion resistance.

---

W pracy przedstawiono wyniki badań morfologii powierzchni (SEM), składu chemicznego (XPS) oraz odporności korozyjnej (LSV) anodowo utlenianych powłok stopowych Zn-Ni elektroosadzanych na podłożu stalowym. Proces utleniania prowadzono w kąpielach, które stanowiły roztwory wodorotlenku sodu i fluorku amonu. Na podstawie przeprowadzonych badań stwierdzono, że w wyniku anodowej obróbki powłok Zn-Ni na ich powierzchni tworzą się powłoki konwersyjne składające się z tlenków i wodorotlenków cynku i niklu oraz fluorków tych metali. Najlepsze z nich charakteryzowały się drobnokrystaliczną warstwą pasywną bez spękań, która znacząco poprawiała odporność korozyjną.