Geometrical parameters and strength of clinching joint formed with the use of an additional rivet

In the publication, the results of an experimental analysis of joint formation by pressing of DX51D steel sheets with thickness of 1.5 (mm) with the use of a rigid punch and an additional deformable rivet of various shapes were presented. The influence of the use of a steel rivet with a diameter d = 5 (mm), similar to the dimensions of the forming punch in the case of the classic clinching variety on the interlock parameters was investigated. The used die was with a four movable segments-dedicated to connections made in the clinch-riveting technology by TOXR PRESSOTECHNIK. In additional, experimental tests were made for joining sheets with a rivet of various shapes, i.e. with a through hole. Joints were formed and the correctness of the upper blockage in the lower sheet was observed on the joints cross-sections. The interlock parameters were measured for each joints samples. In order to compare the influence of using an additional rivet on interlock parameters and joints strength the traditional clinching joints were also made. The minimal thickness of the traditional clinching joint embossment for 2 sheets of 1.5 (mm) thickness for each was X = 0.75 (mm).

---

Opracowanie rekordu ze środków MNiSW, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2024).