Intensification of the transformation of retained austenite to martensite under the influence of change in the stress state in wires of TRIP-type steel

Both the magnitudes and dynamics of the stress state occurring in drawing processes may cause a considerable acceleration of the transformation of retained austenite to martensite in wires of TRIP-type steel. The paper presents an investigation to determine the amount of transformed retained austenite in the structure of wires made of TRIP-type steel resulting from the change in the stress state upon loading the material with cyclical and variable-sign stress under rotary bending conditions. The value of the stress acting on the material was smaller than the value of the proof stress R0.2. The carried out investigations made possible to determine whether and to what extent the loading of wire with cyclical external stresses of magnitudes lower than the R0.2 value might influence the amount of transformed retained austenite and, consequently, the mechanical properties of utility products.

---

Występujące w procesach ciągnienia wartości, jak i dynamika stanu naprężenia może powodować znaczne przyspieszenie przemiany austenitu szczątkowego w martenzyt w drutach ze stali typu TRIP. W pracy przedstawiono badania dotyczące określenia ilości przeminionego austenitu szczątkowego w strukturze drutów ze stali typu TRIP, w efekcie zmiany stanu naprężenia, po obciążeniu materiału, cyklicznym, zmiennym co do znaku naprężeniem w warunkach zginania obrotowego. Wartość naprężeń oddziaływujących na materiał była mniejsza od wartości umownej granicy plastyczności R0,2. Przeprowadzone badania pozwoliły na stwierdzenie, czy i w jakim stopniu obciążenie drutów cyklicznymi naprężeniami zewnętrznymi o wartościach mniejszych od R0,2 może wpływać na ilość przemienionego austenitu szczątkowego, tym samym na własności mechaniczne wyrobów użytkowych.