The paper presents the results of studies of the chromium-molybdenum-vanadium steel designed for operation at elevated temperatures. The material was examined after long-term operation and after the revitalising heat treatment. Studies were performed by conventional methods and small punch test. Curves of ductile-brittle transition were plotted from the Charpy V-notch impact tests and were next compared with the curves of sudden loss of ductility obtained in the small punch test. Additionally, for the material before and after revitalisation, the values of temperatures Tpk and Tnuc were calculated using the method of inflection point.

---

W pracy przedstawiono wyniki badań stali chromowo-molibdenowo-wanadowej przeznaczonej do pracy przy podwyższonych temperaturach. Materiał badano w stanie po wieloletniej eksploatacji i po obróbce cieplnej rewitalizującej. Badania prowadzono z zastosowaniem metod konwencjonalnych oraz przy pomocy metody small punch. Sporządzono krzywe przejścia plastyczno-kruchego z próby udarności Charpy V i porównano je z krzywymi nagłej utraty ciągliwości z próby small punch. Dla materiału przed i po rewitalizacji określono wartości temperatur Tpk i Tnuc stosując metodę punktu przegięcia.