The impact of liquid environments containing Mg2+ and SO42- ions on the durability of cement concrete with limestone aggregates

Carbonate aggregates exposed to a liquid environment may decompose and produce bulking of calcium and magnesium hydroxides. The presence of Ca2+, Mg2+ and SO42- – ions in the corrosive environment and temperature +60ºC may influence the rate of aggregate decomposition. Limestone aggregate, however, is suspected of enhancing concrete properties under contact with aggressive sulphate medium. The paper presents the results of a study on the impact of exposure to the environment containing calcium, magnesium and sulphate(VI) ions in different temperature condition on the susceptibility of selected limestone aggregates to bulking in liquid environment in cement concrete.

---

Kruszywa węglanowe eksponowane w środowisku ciekłym mogą ulegać zniszczeniu z wytworzeniem pęczniejących form wodorotlenku wapnia i magnezu. Obecność jonów Ca2+, Mg2+ i SO42- w środowisku korozyjnym oraz podwyższona temperatura t = +60ºC mogą mieć wpływ na stopień destrukcji tych kruszyw. Jednakże, kruszywa wapienne mogą poprawiać odporność betonu na działanie agresywnego środowiska siarczanowego. W artykule przedstawiono wyniki badań nad wpływem ekspozycji korozyjnej betonów cementowch wykonanych z wybranych kruszyw wapiennych na pęcznienie w środowisku ciekłym zawierającym jony wapnia, magnezu i siarczanu(VI) w zróżnicowanej temperaturze.