Preparation of nanocrystalline composites TiO2-SnO2 by sol-gel method

The paper describes the sol-gel method for preparing nanocomposites from the TiO2-SnO2 system with various chemical compositions. The obtained nanopowders are characterized by a significantly expanded specific surface area (SSA ~ 100 m2/g), which suggests low particles agglomeration and undoubtedly has a beneficial effect on the application of the obtained nanopowders in the production of resistive sensors for gas detection. The crystallites sizes estimated with use of XRD (Dhkl ~ 8 nm) are similar to those calculated based on specific surface area measurements (DBET ~ 15 nm). Moreover, the paper examines the spectral dependence of the diffuse reflection coefficient Rdiff (λ) of the obtained nanocomposites.

---

W pracy opisano metodę zol-żel do otrzymywania nanokompozytów z układu TiO2-SnO2 o różnym składzie chemicznym. Otrzymane nanoproszki charakteryzują się dużym rozwinięciem powierzchni właściwej (SSA ~100 m2/g), co sugeruje słabą aglomerację cząstek i niewątpliwie wpływa korzystnie na zastosowanie otrzymanych nanoproszków do wytwarzania sensorów rezystancyjnych dla wykrywania gazów. Wielkości krystalitów wyznaczone techniką XRD (Dhkl ~ 8 nm) są zbliżone do oszacowanych na podstawie pomiarów powierzchni właściwych (DBET ~ 15 nm). W pracy zbadano również spektralną zależność współczynnika odbicia dyfuzyjnego Rdiff (λ) uzyskanych nanokompozytów.