Welding of DOCOL 1200M using micro-jet cooling
In welding elements of the supporting structure of the means of transport, attention is paid to the high strength and good plastic properties of the welded joint. In the construction of transport means, DOCOL 1200M steel from the AHSS group is increasingly used due to their high tensile strength of steel at the level of 1200 MPa. The welds have much lower strength than the native material. In this paper, it was decided to check the weldability of DOCOL 1200M steel with the use of micro-jet cooling. A positive effect of micro-jet cooling on the mechanical properties of joints made on DOCOL 1200M steel was observed. A positive effect of micro-jet cooling on the mechanical properties of welded joints made of DOCOL 1200M steel has been observed.
Przy spawaniu elementów konstrukcji nośnej środków transportu zwraca się uwagę na wysoką wytrzymałość i dobre własności plastyczne złącza spawanego. W budowie środków transportu coraz częściej stosuje się stal DOCOL 1200Mz grupy AHSS z uwagi na jej dużą wytrzymałość na rozciąganie na poziomie 1200 MPa. Złącza posiadają dużo niższą wytrzymałość od materiału rodzimego. W niniejszym artykule postanowiono sprawdzić spawalność stali DOCOL 1200Mz wykorzystaniem chłodzenia micro-jetowego. Zaobserwowano pozytywny wpływ chłodzenia mikro-jetowego na właściwości mechaniczne złączy spawanych wykonanych na stali DOCOL 1200M.
Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2020).