Rheological and thermal properties of mixtures of hydroxyl-terminated polybutadiene and plasticizer

Mixtures of hydroxyl-terminated polybutadiene (HTPB) and dioctyladipate (DOA) as a plasticizer, which after crosslinking are applied as binders in heterogeneous propellants, were studied.The influence of mixture composition on rheological and thermal properties, important from technological and utility viewpoint were specified. The temperature dependence of prepared mixtures viscosity were studied. Systems were subjected to crosslinking and values of pot life (tpl) were determined. It was stated that tpl rose with increasing plasticizer content. Differential scanning calorimetry and thermogravimetry techniques were used toanalyze thermal stability of mixtures. It was concluded that applied component scould not decompose in the temperature range of 290–350 K and studied mixtures did not cause the hazard of thermal explosion.

---

Zbadano mieszaniny polibutadienu z końcowymi grupami hydroksylowymi (HTPB) oraz adypinianu dioktylu (DOA) jako plastyfikatora, które po usieciowaniu wykorzystywane są jako lepiszcza w heterogenicznych paliwach rakietowych. Określono wpływ składu na reologiczne i termiczne właściwości mieszanin, mające istotne znaczenie z technologicznego i użytkowego punktu widzenia. Zbadano zależność lepkości przygotowanych mieszanin od temperatury. Badane układy poddano sieciowaniu i wyznaczono wartości czasu życia technologicznego (tpl).Wykazano, że tpl wydłuża się ze wzrostem zawartości plastyfikatora. Stabilność termiczną mieszanin zbadano za pomocą różnicowej kalorymetrii skaningowej i termograwimetrii. Stwierdzono, że zastosowane składniki nie ulegają rozkładowi w temperaturze od 290 do 350 K i badane mieszaniny nie powodują zagrożenia eksplozją.

---

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).