Microstructure and properties of dissimilar welded joint between P91 and TP347HFG steels after 105 000 h service

This paper presents the results of investigations of a dissimilar welded joint made between X10CrMoVNb9-1 (P91) martensitic steel and TP347HFG austenitic steel. The welded joint material was taken from a primary steam superheater coil operated at maximum working temperature of approx. 540°C for more than 105 000 hours. Destructive testing and metallographic tests were carried out for the welded joint material to determine the impact of long-term service on the properties of the joint. Microstructure of the welded joint was observed using a optical microscope (OM) and scanning electron microscope (SEM). The destructive testing included: impact test, static tensile test and hardness measurement.

---

W pracy zostały przedstawione wyniki badań złącza spawanego różnoimiennego, wykonanego pomiędzy stalą martenzytyczną w gatunku X10CrMoVNb9-1 (P91), a stalą austenityczną TP347HFG. Materiał złącza spawanego został pobrany z wężownicy przegrzewacza pary świeżej, pracującego w maksymalnej temperaturze pracy około 540oC w czasie ponad 105 000 godzin. Dla materiału złącza spawanego przeprowadzono badania niszczące oraz badania metalograficzne, w celu określenia wpływu długotrwałej eksploatacji na właściwości złącza. Obserwacji mikrostruktury złącza spawanego dokonano za pomocą mikroskopu świetlnego (OM) oraz elektronowego mikroskopu skaningowego (SEM). Badania niszczące obejmowały: próbę udarności, statyczną próbę rozciągania oraz pomiar twardości.