316L-HAp composites synthesized by spark plasma sintering method (SPS)

This article presents the results of studies concerning the production technology and properties of 316L-HAp composite materials sintered at temperatures of 1000 and 1100°C with compaction pressures of 5, 25, and 50 MPa. The spark plasma sintering method (SPS) was applied for the purpose of producing these materials. 316L-HAp composites characterized by densities ranging from 5.45 to 6.01 g/cm3 were the final products of the applied process. The results of absolute porosity measurements are discussed. It is shown that as sintering temperature and compaction pressure increase, so does the sinter's apparent density and compression strength, although an Rc value that is lower by 8% is observed for sinters produced at a temperature of 1100°C compared to those produced at a temperature of 1000°C. Hardness decreases as sintering temperature increases and reaches the highest values in sinters produced with a compaction pressure equal to 25 MPa.

---

Przedstawiono wyniki badań dotyczących technologii wytwarzania i własności materiałów kompozytowych 316L-HAp spiekanych w temperaturze 1000 i 1100°C przy ciśnieniu prasowania 5, 25 i 50 MPa. Do ich wytworzenia zastosowano metodę iskrowego spiekania plazmowego (SPS). Produktem końcowym zastosowanego procesu były kompozyty 316L-HAp charakteryzujące się gęstością wynoszącą od 5,45 do 6,01 g/cm3. Omówiono wyniki pomiarów porowatości całkowitej. Wykazano, iż wraz ze wzrostem temperatury spiekania i ciśnienia prasowania wzrasta jego gęstość pozorna oraz wytrzymałość na ściskanie, przy czym w przypadku kompozytów spiekanych w temperaturze 1100°C obserwuje się mniejszą o 8% wartość Rc niż dla spieków wytworzonych w temperaturze 1000°C. Twardość zmniejsza się wraz ze wzrostem temperatury spiekania, przyjmując największe wartości dla spieków wytworzonych przy ciśnieniu prasowania wynoszącym 25 MPa.