SiC particle distribudtion in castings made from composite suspension A359/SiCp with various casting conditions

The paper presents results of an evaluation of the reinforcing phase particles in identical test castings of small overall dimensions, obtained from a composite suspension in diversified casting conditions. The composite suspension behavior has been studied in different casting conditions: gravitational, gravitational aided by subatmospheric pressure and under centrifugal force. The beneficial influence of the factors intensifying the process of filling mold cavities with a composite suspension was found. Gravitational casting of the composite suspension is limited by the size of the casting modules - in the analyzed experiment conditions they cannot be lower than 1.4 mm. In the castings obtained using subatmospheric pressure, uniform distribution of the reinforcing phase particles was found. Additionally, highly diversified particle distribution was observed in castings from a suspension subjected to centrifugal forces.

---

Przedstawiono wyniki oceny rozkładu cząstek fazy zbrojącej w identycznych odlewach próbnych o małych gabarytach, uzyskanych z zawiesiny kompozytowej w zróżnicowanych warunkach jej odlewania. Zbadano zachowanie się zawiesiny kompozytowej w warunkach odlewania: grawitacyjnego, grawitacyjnego wspomaganego podciśnieniem oraz pod działaniem siły odśrodkowej. Stwierdzono korzystny wpływ czynników intensyfikujących proces wypełniania wnęk form zawiesiną kompozytową. Grawitacyjne odlewanie zawiesiny kompozytowej ograniczone jest wielkością modułów odlewów, które w analizowanych warunkach doświadczeń nie mogą być mniejsze niż 1,4 mm. Stwierdzono równomierny rozkład cząstek fazy zbrojącej w odlewach uzyskanych z wykorzystaniem podciśnienia, a ponadto bardzo zróżnicowany rozkład cząstek w odlewach z zawiesiny poddanej działaniu sił odśrodkowych.