Cyclic oxidation resistance of Co–9Al–9W new cobalt-based superalloy
Cobalt-based superalloys are class of new heat-resistant materials for components of turbine engines. The γ/γʹ phase microstructure similar to nickel-based analogue, provide excellent creep resistance as well as resistance to corrosion and oxidation. Superior high temperature resistance drives intensive development of Co-based superalloys. The aim of paper is assessment of high temperature oxidation behaviour of Co–9Al–9W alloy in as-cast state. The cyclic oxidation performance of Co–9Al–9W alloy was studied at temperature 800°C and 900°C. The cyclic oxidation test was carried out under laboratory air atmosphere with time of exposure 25 hours and multiplicity of it. The scale morphology after cyclic oxidation test was investigated. The evaluation of scale concerned macrostructure, microstructure, chemical and phase composition of surface. Surface of tested alloys after oxidation was characterized using X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and light microscopy (LM). Obtained data revealed that Co–9Al–9W alloy showed acceptable resistance to cyclic test at temperature 800°C. The oxide scale at this variant showed mainly Co oxides as an dominant phase. At higher temperature – 900°C the strong effect of spallation of scale was observed as results of CoWO4 complex oxide formation.
Celem pracy była charakterystyka odporności na utlenianie nowego typu stopów na bazie kobaltu umacnianych fazą Co3(Al, W). Ocenie poddano stop Co–9Al–9W (% at.) w stanie po odlaniu i homogenizacji. Wykonano próby odporności na utlenianie cykliczne w cyklach 25-godzinnych w atmosferze powietrza. Zakres prezentowanych badań obejmował pomiary masy próbek po kolejnych cyklach, ocenę stanu powierzchni z uwzględnieniem procesów jej odpadania, jak również charakterystykę składu chemicznego i fazowego powstałej zgorzeliny oraz jej budowę morfologiczną.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).