Microstructure and phase composition of NiAl-CrB2 composite powders used for plasma spraying
The preparation of powder agglomerates used in the plasma spray deposition processes, and especially their homogeneity, turned out to be highly important at the moment when the phase ratio in the composite coatings began to differ from that in the starting materials. The present experiment was aimed at comparing the microstructure and phase composition of hot pressed or sintered NiAl and CrB2 powders. The use of SEM and XRD methods showed that only sintering leads to a reaction of the chromium diboride with the intermetallic matrix. As a result of this process, Ni0.5Cr1.5B3 phase precipitates on the CrB2 particles. Consequently, the agglomerates formed after crushing the compacts obtained by sintering are much more homogeneous than those formed by hot pressing.
Przygotowanie aglomeratów proszków wykorzystywanych w procesach natryskiwania plazmowego, a w szczególności ich ujednorodnienie, okazało się wysoce istotne w momencie, gdy skład powłok kompozytowych zaczął się znacząco różnić od stosunku udziałów proszków wyjściowych. Obecny eksperyment był nakierowany na porównanie mikrostruktury i składu fazowego proszków NiAl oraz CrB2 spiekanych w stanie stałym pod ciśnieniem (hot pressed) oraz z przetopieniem osnowy metalicznej (sintered). Zastosowanie mikroskopii skaningowej i dyfraktometrii rentgenowskiej wykazało, że tylko przetopienie osnowy prowadzi do reakcji pomiędzy nią a dwuborkiem chromu. W rezultacie tego procesu dochodzi do wydzielania na CrB2 fazy typu Ni0.5Cr1.5B3. Aglomeraty powstałe po rozdrobnieniu spieków uzyskanych na drodze z przetopieniem osnowy są znacznie bardziej jednorodne niż te otrzymane z wykorzystaniem prasowania na gorąco.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).