Analysis of the hot upsetting process between flat plates with high reductions of the material used for forged ingots with pierced holes was performed. The analysis was done by means of computer code FORM2D simulation. lt was found that the main cause of occurrence of discontinuities in shape of overlapping and ring-like craeks on the front surface of forged ingots adjoining to side surfaces is superimposition of unfavourable phenomena. The phenomena in question are the zone of lowered temperature and accompanying lowered plasticity of material, causing fold generation, and boundaries of crystallisation zones during solidification of ingot.

---

Dokonano analizy procesu spęczania na gorąco między płaskimi płytami z dużym gniotem materiału stosowanego na odkuwki z otworami. Analizę przeprowadzono w oparciu o symulację komputerową programem FORM2D. Stwierdzono, że główną przyczyną pojawiania się nieciągłości w postaci zakuć i pęknięć pierścieniowych na powierzchni czołowej odkuwek w pobliżu powierzchni bocznej jest nakładanie się niekorzystnych zjawisk, tj. strefy obniżonej temperatury oraz towarzysząca temu zjawisku obniżona plastyczność materiału, powodujących powstawanie fałd, a także granic stref krystalizacyjnych powstałych podczas krzepnięcia wlewka.