Analysis of Dependencies of Woven Fabric’s Breaking Force and Elongation at Break on its Structure Parameters

In this article, the woven fabric weave factor P1 and the integrated fabric structure factor φ, suggested by Milašius, are described. Their qualities are emphasised in comparison with other woven fabric factors. The research results of the woven fabric structure’s influences on its breaking force and elongation at break are also presented in this article; in other words, the dependence of the above-mentioned woven fabric factors on these parameters are presented. The research performed shows that there is no correlation between the weave factor and woven fabric breaking force, although the range of resulting points is wide. As the woven fabric rigidity of weave increases, the weave factor P1 decreases, and the woven fabric elongation at break increases. The integrated fabric structure factor φ which evaluates all parameters of the fabric structure, such as warp and weft materials, warp and weft linear densities, warp and weft settings and the fabric weave, also has similar tendencies of dependence.

---

W artykule przedyskutowano stosowanie współczynnika splotu P1 oraz zespolonego współczynnika strukturalnego φ zaproponowanego przez Milašiusa. Ich zalety zostały podkreślone w porównaniu z innymi współczynnikami opracowanymi dla tkanin. Przeprowadzono analizę wpływu struktury tkanin na siłę zrywającą i wydłużenie przy zerwaniu, a więc także na zależność tych parametrów od dyskutowanych współczynników. Stwierdzono, że nie ma korelacji pomiędzy współczynnikiem splotu a siłą zrywającą, pomimo dużego zakresu przebadanych wartości. Przy wzroście sztywności tkaniny współczynnik splotu tkaniny P1 zmniejsza się, a wydłużenie przy zerwaniu rośnie. Zespolony współczynnik strukturalny φ wykazuje podobne tendencje zależności, co pozwala na ocenę wszystkich parametrów struktury tkaniny, w tym takich jak liczność osnowy i wątku oraz zastosowany splot.