Microstructural Characterization of Quenched and Plastically Deformed Two-Phase α+β Titanium Alloys

Development of microstructure in two-phase α+β titanium alloys is realized by thermomechanical processing – sequence of heat treatment and plastic working operations. Analysis of achieved results indicates that hot plastic deformation – depending on deformation degree – causes significant elongation of α phase grains. Following heat treatment and plastic deformation processes lead to their fragmentation and spheroidization. Characterization of microstructure morphology changes during thermomechanical processing of quenched Ti-6Al-4V and Ti-6Al-2Mo-2Cr alloys is presented in the paper. The effect of martensitic phase α’(α”) on microstructure development in plastic deformation process was confirmed.

---

Kształtowanie mikrostruktury dwufazowych stopów tytanu α+β realizowane jest w procesie cieplno-plastycznym będącym sekwencją operacji obróbki plastycznej i przeróbki plastycznej. Analiza uzyskanych wyników badań wskazuje, że odkształcanie plastyczne na gorąco – w zależności od stopnia odkształecenia - powoduje wydłużanie ziarn fazy α. Kolejne operacje obróbki cieplnej lub odkształcania plastycznego prowadzą do ich fragmentacji i sferoidyzacji. W pracy przedstawiono charakteryzację zmian morfologii składników mikrostruktury stopów Ti-6Al-4V oraz Ti-6Al-2Mo-2Cr poddanych przechładzaniu na początkowym etapie procesu cieplno-plastycznego. Potwierdzono oddziaływanie fazy martenzytycznej α’(α”) w badanych stopach na przebieg procesu kształtowania ich mikrostruktury podczas odkształcania plastycznego.