The influence of temperature on selected strength properties of furniture particleboard

The influence of temperature on selected strength properties of furniture particleboard. As a part of the study, the influence of temperature on selected properties of furniture particleboard was tested. P2 type industrial particleboards in three finishing options: raw boards (1), boards covered with melamine film in white (2) and black (3) (10 samples per variant) have been subjected to temperatures from -20oC to +120oC, at 10oC intervals. The Time of exposure for individual temperatures was 7 days. MOR, MOE and IB were determined for tested boards. It has been shown that temperatures above 50oC have a negative effect on strength properties of boards. A large decrease in all tested parameters was observed in the temperature range from +60oC to +120oC. It was also noted that finishing boards with melamine film did not improve their durability.

---

Wpływ temperatury na wybrane właściwości wytrzymałościowe meblowych płyt wiórowych. W ramach pracy zbadano wpływ temperatury na wybrane właściwości meblowych płyt wiórowych. Przemysłowe płyty wiórowe typu P2 w trzech wariantach wykończenia: płyty surowe (1), płyty pokryte filmem melaminowym w kolorze białym (2) i w kolorze czarnym (3) (po 10 próbek na wariant) zostały poddane działaniu temperatur od -20oC do +120oC, z od stopniowaniem, co 10 K. Czas oddziaływania poszczególnych temperatur wynosił 7 dni. Dla badanych płyt oznaczono MOR, MOE. IB, odporności laminatu na pękanie. Wykazano, że temperatura powyżej +50oC wywiera negatywny wpływ na właściwości wytrzymałościowe płyt. Zaobserwowano duży spadek wszystkich badanych parametrów w przedziale temperatur od +60oC do +120oC. Stwierdzono również, że wykończenie płyt filmem melaminowym nie wpływa na poprawę ich wytrzymałości.