Physical Simulation of Individual Heat-Affected Zones in S960MC Steel

This research is focused on the analysis of heat-affected sub-zones in 2 mm thick steel S960MC samples, with the aim of observing and evaluating the mechanical properties after exposure to temperatures corresponding to individual heat-affected sub-zones. Test samples were prepared using a Gleeble 3500 thermo-mechanical simulator. The samples were heated in the range from 550°C to 1350°C and were subsequently quickly cooled. The specimens, together with the base material, were then subjected to tensile testing, impact testing, and micro-hardness measurements in the sample cross-section, as well as evaluation of their microstructure. Fracture surfaces are investigated in samples after impact testing. The heat-affected sub-zones studied indicate high sensitivity to the thermal input of welding. There is a significant decrease in tensile strength and yield strength at temperatures around 550°C.

---

1. This research was funded by APVV, grant number APVV-16-0276; KEGA, grant number KEGA 009ŽU-4/2019; and VEGA, grant number VEGA 1/0951/17. The authors hereby thank these agencies for their support.

---

2. Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2021).