Diffusion AISi-MeCrAlY coatings obtained on intermetallic y-TiAl phase

Purpose: The development of new protective coatings for TiAl intermetallics was conducted. The MeCrAlY-AlSi slurry was used with different amount of aluminium-silicon powder in the binder. Design/methodology/approach: The slurry consisting of aluminium and silicon powder with the addition of MeCrAlY powder were used during the procedure. The inorganic solution made from chromic and phosphoric acid was applied as a binder. The preliminary research of microstructure of obtained coatings was conducted. Findings: The obtained coating consisting of 3 or 4 zones (depending on chemical composition of the slurry) was obtained during the annealing process (950°C/4h). Research limitations/implications: The research results revealed the possibility of obtaining coatings with complex phase and chemical composition. Practical implications: Many problems connected with sedimentation of heavier MeCrAlY powder were observed. Originality/value: The copletele new technologies was described in article.