The causes of high-temperature corrosion in iron casting

In the iron castings with the horizontal or cylindrical surface, in the highest places, the high- temperature corrosion of surface has been confirmed. Metallographic examinations have been carried out and it has been found that in the structure of boundary layer in the scale zone appeared corrosion at the borders of grains. Sand mould with bentonite which was poured with high superheating cast grey iron can cause high temperature corrossion on castings surfaces. The crystal water and structural water contented in bentonite and also high temperature of pouring metal can create intensive oxidizing atmosphere. Hydrogen pressurization, which dissolve in metal and in non metallic inclusions can accelerate corrossion process. During the temperature reducing educed hydrogen can cause micro-cracks which increase the surface of high temperature oxidation.

---

W odlewach z żeliwa szarego z poziomą lub cylindryczną powierzchnią, w miejscach położonych najwyżej w formie, stwierdzono występowanie korozji wysokotemperaturowej. Badania metalograficzne wykazały, że pod warstwą skorodowaną korozja występuje na granicach ziaren i postępuje w głąb od powierzchni odlewu. Zalewanie form piaskowych z bentonitem wysoko przegrzanym żeliwem starym może stanowić przyczynę występowania korozji wysoko temperaturowej na powierzchni odlewów. Woda krystaliczna i strukturalna zawarta w bentonicie oraz wysoka skala przegrzania metalu powodują atmosferę silnie utleniającą. Zwiększona przy tym ilość wodoru, który rozpuszcza się w metalu i we wtrąceniach niemetalicznych przyspiesza procesy korozyjne. Przy obniżaniu temperatury wodór wydziela się powodując mikropęknięcia, które zwiększają powierzchnie utleniane.