Structural features of poly(3-hydroxybutyrate) with an ethylene-propylene copolymer blends

The methods of DSC and IR spectroscopy were used to study various blends of poly(3-hydroxybutyrate) (PHB) with ethylene-propylene copolymer rubber (EPS). When the weight fractions of the initial polymers are equal, a phase inversion takes place; as the blends are enriched with EP, the degree of crystallinity of poly(3-hydroxybutyrate) decreases. In blends, the degradation of poly(3-hydroxybutyrate) begins at a lower temperature compared to the pure polymer and the thermooxidative activity of the ethylene-propylene copolymer in the blend decreases in comparison with the pure copolymer.

---

Mieszaniny poli(3-hydroksymaślanu) (PHB) i kopolimeru etylenowo-propylenowcgo (EP), o różnych proporcjach składników, badano metodami DSC i spektroskopii IR. W przypadku, gdy udziały wagowe wyjściowych polimerów są równe, obserwuje się zjawisko inwersji fazowej; jeżeli mieszaniny zawierają więcej EP stopień krystaliczności poli(3-hydroksy maślanu) zmniejsza się. Degradacja poli(3-hydroksymaślanu) zawartego w mieszaninach rozpoczyna się w temperaturze niższej niż samego polimeru, natomiast degradacja termooksydacyjna kopolimeru etylenowo-propylenowego zmniejsza się w porównaniu z czystym polimerem.