Mechanical Properties of Material Extrusion Printed Samples Made of PLA After Treatment in an Acetone Bath

This paper presents a study of the effect of chemical treatment using pure acetone on strength specimens made from PLA polylactide produced by 3D FDM/FFF printing technology. The strength specimens were designed in accordance with the ISO 527 standard. The chemical treatment was carried out using baths at different time intervals. The hardness of the samples was measured, and a tensile test was performed. The results show that with prolonged contact with acetone, the hardness of the material decreases by approximately 45% compared to untreated samples. When analysing the tensile tests, it was noted that the tensile strength decreases with longer chemical bath time. At the same time, the material becomes more ductile, resulting in a high elongation at break in tension of up to 40% relative to untreated samples.

---

W artykule przedstawiono badanie wpływu obróbki chemicznej przy użyciu czystego acetonu na wytrzymałość próbek wykonanych z polilaktydu PLA w technologii druku 3D FDM/FFF. Próbki wytrzymałościowe zostały zaprojektowane zgodnie z normą ISO 527. Obróbkę chemiczną w roztworze acetonu przeprowadzono w różnych odstępach czasu. Zmierzono twardość próbek i przeprowadzono statyczną próbę rozciągania. Wyniki wskazują, że przy dłuższym kontakcie z acetonem twardość materiału spada o około 45% w porównaniu z próbkami niepoddanymi obróbce. Analizując testy rozciągania, zauważono, że wytrzymałość na rozciąganie zmniejsza się wraz z wydłużeniem czasu trwania kąpieli chemicznej. Jednocześnie materiał staje się bardziej plastyczny, co powoduje, że wydłużenie przy zerwaniu jest o 40% większe w porównaniu do próbek niepoddanych obróbce chemicznej.