The influence of fabrication conditions on the physical properties of PLZT:Nd3+ ceramics

The aim of this work was to study the effect of fabrication conditions and neodymium co-doping on the physical properties of (Pb0.98La0.02)(Zr0.65Ti0.35)0.98O3, known as PLZT:Nd3+ ceramics. All ceramic powders of these materials were synthesized by the conventional mixed oxide method, from the high purity raw materials (>99.9%). The bulk ceramic samples were sintered by the pressure less sintering and the hot-uniaxial pressing techniques. The study gives a detailed account of the relationships between doping and preparing conditions on the dielectric and optical properties of obtained ceramic materials. Optimal conditions of PLZT:Nd3+ preparation as well as Nd3+ activator concentration were determined in relation to the potential opto-electronic applications.

---

Celem niniejszej pracy było zbadanie wpływu warunków wytwarzania i zastosowanej domieszki neodymu na właściwości fizyczne ceramiki (Pb0.98La0.02)(Zr0.65Ti0.35)0.98O3, określanej mianem PLZT:Nd3+. Wszystkie proszki przygotowanych składów syntetyzowano metodą konwencjonalną, z tlenków o wysokiej czystości (>99.9%). Próbki ceramiczne zagęszczano techniką swobodnego spiekania i jednoosiowego prasowania na gorąco. Wykonane badania dały szczegółowy opis zależności między stosowaną domieszką oraz przyjętymi warunkami wytwarzania oraz wpływu na dielektryczne i optyczne właściwości otrzyma- nych materiałów ceramicznych. Optymalne warunki przygotowania PLZT:Nd3+, jak również zastosowane stężenia aktywatora Nd3+ zostały określone w odniesieniu do potencjalnych zastosowań optoelektronicznych.