Testing of residual material created in the process of zinc recovery from steelmaking dust
The paper presents the results of research on the analysis of material remaining after the recovery of zinc from steelmaking dust. Steelmaking dust from the electric steelworks was used for the tests. The average content of zinc oxide contained in the dust was 35% wt. The reduction process of zinc oxide was carried out in a laboratory resistance furnace under argon. The coke breeze was used for the reduction. The material remaining after the reduction was melted in a laboratory induction furnace. As a result of the process, a metallic alloy was obtained, which was a subject of a further chemical analysis.
W pracy przedstawiono wyniki badań dotyczących analizy materiału pozostałego po odzysku cynku z pyłów stalowniczych. Do badań użyto pyłów stalowniczych pochodzących z elektrostalowni. Średnia zawartość tlenku cynku zawartego w pyłach wynosiła 35% mas. Proces redukcji tlenku cynku przeprowadzono w laboratoryjnym piecu oporowym, w atmosferze argonu. Do redukcji wykorzystano koksik. Pozostały po redukcji materiał przetopiono w laboratoryjnym piecu indukcyjnym. W wyniku procesu otrzymano stop metaliczny, który poddano dalszej analizie chemicznej.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).