Effect of the powder consolidation with biopolymer on the corrosion characteristics of bonded magnets based on Nd-(Fe,Co)-B
In this paper the effect of the Nd-(Fe,Co)-B powder particles consolidation process with difrent types of organic resin on the corrosion resistance of the bonded magnets in the aggressive environments was presented. The tests were carried out on the magnetic material based on Nd12Co5Fe77B6 powder consolidated with two types of resin (termo-setting epoxy resin and chemicalsetting biopolymer). Impact of the used consolidation process was rated on the basis of polarization curves recorded in: sulphate enviroment (pH = 3), phosphate enviroment (pH = 3), as well as in phosphate environment with chloride ions (Cl-) and Ringer solution (pH = 6) assigned during electrochemical measurements of polarization resistance. It has been found that the consolidation of powder particles with biopolimer has a beneficial effect on the corrosion resistance of the final magnetic material.
W artykule przedstawiono wpływ procesu konsolidacji cząstek proszku Nd-(Fe,Co)-B różnymi typami żywic organicznych na odporność korozyjną wiązanych magnesów w środowiskach agresywnych. Do badań posłużono się wiązanymi materiałami magnetycznymi na bazie proszku Nd12Co5Fe77B6 wiązanych dwoma rodzajami spoiwa (termoutwardzalna żywica epoksydowa i chemoutwardzalny biopolimer).Wpływ procesu konsolidacji żywicami organicznymi oceniono na podstawie badań elektrochemicznych w środowisku: siarczanowym (pH = 3), fosforanowym (pH = 3), w fosforanowym z dodatkiem jonów chlorkowych (Cl-) oraz w roztworze Ringera (pH = 6). Stwierdzono, że proces konsolidacji proszku biopolimerem korzystnie wpływa na odporność korozyjną finalnego materiału magnetycznego.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.