Modifying of Polyester Fabric Surface with Polyelectrolyte Nanolayers Using the Layer-by-layer Deposition Technique

Polyelectrolytes such as poly(4-vinylpyridine) and poly(acrylic acid) with opposite charges have been deposited on a polyester fabric by the layer-by-layer technique. The first acidic layer with carboxylic groups were produced by grafting acrylic acid onto the polyester fabric according to the previously established grafting conditions. Selected fibre properties connected with the character of the deposited nanolayer of polyelectrolyte were tested. It has been found that the content of methylene blue dye in fibre and water retention depend on the character of the deposited nanolayer, as they are always considerably higher when the top nanolayer consists of poly(acrylic acid). Electron microscope photographs show that the fibre surface in the fabric becomes smoother after polyanion and polycation nanolayers are deposited.

---

W pracy badano wytwarzanie multiwarstw na tkaninie poliestrowej na drodze kolejnego nanoszenia warstw polielektrolitów – poli(4-winylopirydyny) i poli(kwasu akrylowego) o przeciwnych ładunkach w wyniku ich elektrostatycznego oddziaływania. Pierwszą kwasową warstwę z grupami karboksylowymi wytwarzano na drodze szczepienia tkaniny poliestrowej kwasem akrylowym, ustalając uprzednio optymalne warunki szczepienia tkaniny poliestrowej. Badano zmianę wybranych właściwości, związanych z charakterem naniesionej warstwy z polielektrolitu. Stwierdzono, że zawartość barwnika – błękitu metylenowego we włóknie oraz wartość retencji wody zależą od charakteru naniesionej warstwy i były wyraźnie wyższe w przypadku gdy wierzchnią warstwę stanowił poli(kwas akrylowy). Zdjęcia mikroskopowe elektronowe pokazują, że powierzchnia włókien w tkaninie staje się gładsza po naniesieniu warstw polianionu i polikationu.