Effects of Precipitation Hardedning in Co-Ni-Cr Alloy on Dissipative Motion of Dislocations by Amplitude-Dependent Internal Friction Measurements
The effects of precipitation hardening occurring in a Co-Ni-Cr alloy after annealing treatments have been studied by using mechanical spectroscopy. The amplitude-dependent internal friction (ADIF) due to the dissipative motion of dislocations reveals the presence of a threshold strain for weakly pinned dislocations. The change of ADIF curves and the increase of the elastic modulus after thermal cycles producing precipitates suggest that dislocations motion is hindered leading to increasing strength of the material. Precipitation is confirmed by the changes of thermoelectric power (TEP) and by hardness measurements showing a hardness increase at the same temperature as the maximum in TEP curve. The ADIF spectra as well as the interaction between dislocations and precipitates are interpreted by proposing a phenomenological model based on the Granato-Lücke theory.
Wpływ utwardzania wydzieleniowego występującego w stopie Co-Ni-Cr po wyżarzaniu zbadano za pomocą spektroskopii mechanicznej. Wewnętrzne tarcie zależne od amplitudy (ADIF) ze względu na rozpraszający ruch dyslokacji ujawnia obecność naprężenia granicznego dla słabo zakotwiczonych dyslokacji. Zmiana krzywych ADIF i wzrost modułu sprężystości po obróbce cieplnej wytwarzającej wydzielenia wskazują, że ruch dyslokacji jest utrudniony prowadząc do zwiększenia wytrzymałości materiału. Wydzielenia są potwierdzone przez zmiany siły termoelektrycznej i pomiary twardości, wykazujące zwiększenie twardości w tej samej temperaturze, co maksimum na krzywej TEP. Widma ADIF, a także oddziaływania między dyslokacjami i wydzieleniami są interpretowane przez proponowany fenomenologiczny model oparty na teorii Granato-Lücke.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.