Experimental study of the basic mechanical properties of hardened gypsum paste modified with addition of polyoxymethylene micrograins
The development of the construction industry and the growing ecological awareness of society encourages us search for new solutions to improve building materials. Therefore, an attempt was made to improve building gypsum by modifying it with the addition of polyoxymethylene (POM). Polymer grains, with a particle size below and above 2 mm, were added to the samples in the amount of 1% and 2% relative to gypsum. The work contains the results of bending and compressive strength tests of prepared gypsum beams. It was shown that the compressive strength increased by 7% and the bending strength increased by 31% when compared to the reference test without the addition of polymer. All the obtained gypsum composites were characterized by a growth of strength. The best results were obtained for the sample containing gypsum composite modified with polymer in the amount of 1% and with a diameter of grains below 2 mm.
Głównym celem pracy było sprawdzenie możliwości wykorzystania odpadów polioksymetylenowych (POM) w celu zwiększenia wytrzymałości na zginanie i ściskanie zaprawy gipsowej. Autorzy założyli, że polioksymetylen znacznie poprawi właściwości mechaniczne modyfikowanego gipsu. Ponadto przyjęto w badaniach, że wielkość ziaren polimeru może mieć wpływ na właściwości mechaniczne gipsu. W literaturze jest niewiele badań dotyczących modyfikacji materiałów budowlanych z dodatkiem polioksymetylenu. Większość z nich dotyczy jednak betonu. W związku z tym istnieje potrzeba zbadania wpływu POM na właściwości gipsu.
Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2020).