Silver nanoparticles in isotactic polypropylene (iPP). Part I. Silver nanoparticles as metallic nucleating agents for b-iPP polymorph

Isotactic polypropylene (iPP) nanocomposites containing 0.1, 0.2, 0.4 and 0.6 wt % of silver nanoparticles (nAg) were prepared by melt compounding in a one-screw extruder. Selected samples were isothermally recrystallized at different temperatures 50, 75, 100, 125, 130 and 135 °C, and under non-isothermal conditions. The size of the silver particles dispersed in the iPP matrix were estimated by ultraviolet/visible spectroscopy (UV-VIS). The effects of nAg additions on the structure of the iPP were studied by wide angle X-ray scattering (WAXS) and differential scanning calorimetry (DSC) techniques. The results clearly indicate that the addition of nAg induces the formation of the ß-iPP polymorph. It is shown that the relative amount of the b form in the recrystallized nanocomposites depends on both the concentration of silver nanoparticles and thermal conditions of recrystallization.

---

Nanokompozyty zawierające 0,1, 0,2, 0,4 oraz 0,6 % mas. nanocząstek srebra (nAg) w matrycy izotaktycznego polipropylenu (iPP) otrzymano w procesie wytłaczania za pomocą wytłaczarki jednoślimakowej. Próbki poddano rekrystalizacji w warunkach izotermicznych, w temp. 50, 75, 100, 125, 130 i 135 °C oraz rekrystalizacji nieizotermicznej. Wymiary cząstek srebra rozproszonych w matrycy iPP określano metodą spektrometrii UV/VIS. Wpływ nanocząstek srebra na formowanie struktury nadcząsteczkowej izotaktycznego polipropylenu oceniano techniką szerokokątowej dyfrakcji promieni rentgenowskich (WAXS) oraz różnicowej kalorymetrii skaningowej (DSC). Badania wykazały, że dodane cząstki Ag przyczyniają się do powstawania formy b w matrycy iPP. Względna zawartość tej polimorficznej odmiany w matrycy iPP zależy od stężenia nanocząstek srebra w rekrystalizowanym nanokompozycie oraz warunków termicznych procesu rekrystalizacji.