Welding of Steel Sheets with Zinc Protective Coatings versus the Emission of Welding Fumes into the Work Environment
The article presents the results of tests aimed to assess the effect of the gas-shielded metal arc welding of protectively coated sheets on the emission of welding fumes (CO, NOx). The tests made it possible to identify the correlation between the welding method, protective coating type, current parameters and filler metals and the emission of pollutants. The tests involved the MAG, CMT, ColdArc and AC MIG Pulse welding of steel sheets provided with various protective (anticorrosive) coatings. The filler metals used in the tests were solid wire grade G3Si1 having a diameter of 1.2 mm and metallic flux-cored wire grade T3T Z M M 1 H15 having a diameter of 1.2 mm.
Przedstawiono badania których celem była ocena wpływu parametrów technologicznych spawania łukowego elektrodą topliwą blach stalowych z powłokami ochronnymi na wielkość emisji pyłu i gazów (CO, NOx). Wyznaczono korelacje pomiędzy metodą spawania, rodzajem powłoki ochronnej, parametrami prądowymi, rodzajem materiału dodatkowego a emisją zanieczyszczeń. Badania prowadzone były dla spawania metodami MAG, CMT, ColdArc oraz AC MIG Pulse blach stalowych z różnymi rodzajami powłok ochronnych antykorozyjnych. Jako materiał dodatkowy zastosowano drut lity w gat. G3Si1 o śr. 1,2 mm oraz drut proszkowy z wypełnieniem metalicznym o oznaczeniu T3T Z M M 1 H15 o śr. 1,2 mm.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).
Wersja polska artykułu w wydaniu papierowym s. 141-148.