Properties of metahalloysite-based geopolymer composites reinforced with steel fibres

This article presents the results of tests on water absorption, compressive strength, and flexural tensile strength of metahalloysite-based geopolymer composites with an activator composed of sodium silicate and 8M NaOH, used in varying weight ratios ranging from 1 to 3. Steel fibres up to 0.75 per cent by volume were added to the geopolymers. The geopolymers were cured for 28 days in water or in air at temperature of 20°C±2°C. The paper also includes microstructure images of the geopolymer mortar reinforced with steel fibres. The results showed that the mortars cured in water exhibited lower 28-day flexural tensile strength and compressive strength compared to the samples stored in air. The addition of steel fibres in amounts up to 0.75% by volume led to an increase in flexural tensile strength of up to approximately two times relative to the fibre-free reference.

---

W artykule przedstawiono wyniki badania nasiąkliwości wagowej, wytrzymałości na ściskanie oraz rozciąganie przy zginaniu kompozytów geopolimerowych z metahaloizytu z aktywatorem o zmiennym stosunku wagowym sodowego szkła wodnego do 8M NaOH wynoszącym od 1 do 3. Do geopolimerów dodano włókna stalowe w ilości do 0,75% obj. Geopolimery dojrzewały przez 28 dni w wodzie lub powietrzu w temperaturze 20°C±2°C. W artykule zamieszczono także obrazy mikrostruktury zaprawy geopolimerowej z włóknem stalowym. Wyniki wykazały, że zaprawa dojrzewająca w wodzie charakteryzuje się mniejszą 28-dniową wytrzymałością na rozciąganie przy zginaniu oraz wytrzymałością na ściskanie w porównaniu z próbkami przechowywanymi w powietrzu. Dodatek włókien stalowych w ilości do 0,75% objętościowo powoduje ok. dwukrotne zwiększenie wytrzymałości na rozciąganie przy zginaniu w odniesieniu do wytrzymałości bez dodatku włókien.