The effect of hollow glass microspheres on the properties of high silica glass fiber fabric/liquid silicone rubber composite sheet
In this study, high silica glass fiber fabric/liquid silicone rubber (HSGFF/LSR) composite sheet filled with hollow glass microspheres (HGM) was prepared. The effects of HGM content on the mechanical, thermal insulation and dynamic mechanical properties of the composite sheet were investigated. The results showed that the compatibility and interfacial properties between HGM and the matrix were improved after the HGM was treated with a silane coupling agent, KH550. Composite, in which the HGM content was 7 % by weight, shows the most advantageous mechanical, insulating and damping properties.
Na bazie tkaniny z włókien kwarcowych (HSGFF) nasyconej ciekłym kauczukiem silikonowym (LSR) otrzymywano kompozyty napełniane mikrosferami szklanymi (HGM). Badano wpływ dodatku mikrosfer na właściwości mechaniczne, izolacyjność cieplną i właściwości dynamiczno-mechaniczne kompozytowych arkuszy. Stwierdzono, że modyfikacja mikrosfer szklanych za pomocą silanowego czynnika sprzęgającego KH550 poprawiła kompatybilność i oddziaływania międzyfazowe cząsteczek HGM i nasyconej ciekłym kauczukiem tkaniny z włókien szklanych. Najkorzystniejsze właściwości mechaniczne, izolacyjne i tłumiące wykazywał kompozyt, w którym zawartość HGM wynosiła 7 % mas.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).