Structural examinations of wood-polymer composites

This paper presents the results of examinations of wood-polymer composites based on mixed polypropylene (PP) and sawdust. Composites with a different volumetric content of wood were prepared (25, 50 and 70% filler). Injection molding technology was used to obtain the research samples. The authors also employed X-ray diffraction, an optical microscope and a transmission scanning microscope. Based on the X-ray diffraction analysis, the presence of several polymorphic forms of the polypropylene were found in the composites used in the study. The crystalline fraction of the matrix in the studied composites is composed of an α phase which crystallizes in a monoclinic lattice and a β phase which crystallizes in a hexagonal system. Microscopic analysis revealed irregular distribution of the wood particles in the matrix of the tested composites.

---

W artykule przedstawiono wyniki badań struktury kompozytów polimer-drewno, gdzie jako napełniacz wykorzystano trociny drzew liściastych i iglastych. Osnowę kompozytu stanowił termoplastyczny polipropylen. Do badań przygotowano kompozyty o różnej frakcji zastosowanych trocin i zmieniającą się zawartością napełniacza (25, 50 oraz 70% obj.). Próbki przygotowano z wykorzystaniem technologii wtryskiwania. Do badań wykorzystano dyfraktometr rentgenowski oraz mikroskopię optyczną i elektronową mikroskopię skaningową. Przeprowadzone badania rentgenowskie pozwoliły zidentyfikować fazy krystaliczne występujące w polimerowej osnowie. Widoczne na dyfraktogramach refleksy dyfrakcyjne pochodzą od odmian polimorficznych polipropylenu: α (jednoskośna) i β (heksagonalna). Analiza mikroskopowa wykazała nierównomierne rozmieszczenie cząstek drewna w osnowie badanych kompozytów.