X-ray Investigations of the Biodegradation Capacity of PBSA in LDPE/PBSA Blends

The interdependence between the crystallinity of poly(butylene succinate-co-adipate) (PBSA) and its biodegradation capacity in blends with low-density polyethylene LDPE has been studied. The LDPE/PBSA blends were prepared by extrusion. As a compatibilizing agent, block copolymer polystyrene-block-poly-(ethylene-co-butylene)-block-polystyrene (FG) modified by maleic anhydride was used. The biodegradation test was performed in a soil and the crystallinity was analysed by the WAXS method. It was found that, six months after the test in question, the degradation of the crystalline part of PBSA took place. In the presence of FG, the PBSA degraded more rapidly due to the lower degree of crystallinity of the polyester.

---

Analizowano zależność między krystalicznością poli(bursztynianu-co-adypinianu butylenu) (PBSA), a jego zdolnością do biodegradacji w mieszaninach z polietylenem niskiej gęstości (LDPE). Mieszaniny LDPE/PBSA otrzymano metodą wytłaczania. Jako środek wiążący zastosowano kopolimer blokowy polistyren-b-(etylen-co-butylen)-b-polistyren szczepiony bezwodnikiem maleinowym (FG). Test biodegradacji mieszanin LDPE/PBSA wykonano w glebie. Stopień krystaliczności składników mieszanin badano za pomocą szerokokątowego promieniowania rentgenowskiego (WAXS). Badanie WAXS wykazało, że po sześciu miesiącach biodegradacji w glebie, degradacji uległa również faza krystaliczna poliestru. Dodatek środka wiążącego FG spowodował, że PBSA podczas testu ulegał biodegradacji w sposób bardziej gwałtowny. Było to spowodowane obniżeniem stopnia krystaliczności poliestru w obecności FG.