Modelling of the structure and mechanical properties of 32CDV13 steel under glow-discharge nitriding for the industrial technology application
The manufacturing of surface layers are increasingly used in industry, as the effective method of improving the useful properties of the machine parts. The specific properties of the nitrided layers such as low temperature of process may be an alternative to the commonly used technology like high-temperature carburizing or carbonitriding in the aerospace industry. The article presents the results obtained after nitriding of complex samples made with 32CDV13 steel. As our research improves the properties of surfaces can be controlled by the process parameters as temperature, duration time, composition of the reactive atmosphere, the pressure (vacuum) and the activation of the surface by cathode sputtering process in the initial stage of the treatment.
Celem pracy było przedstawienie charakterystyk materiałowych i właściwości użytkowych warstw wytworzonych w warunkach wyładowania jarzeniowego na potencjale katody w zależności od parametrów technologicznych. Uzyskane wyniki badań wykazują możliwość kształtowania struktury i składu fazowego, stanu naprężeń własnych warstw azotowanych wytwarzanych na stali 32CDV13. Tym samym właściwości takich jak: twardość, odporność korozyjna, odporność na zużycie przez tarcie, wytrzymałość na rozciąganie, wytrzymałość zmęczeniowa. Jest to proces energooszczędny, który w znaczący sposób zwiększa właściwości użytkowe stali 32CDV13 z zachowaniem jej twardości po obróbce cieplnej rzędu 40÷44 HRC i gwarantuje możliwość pracy przy dużych obciążeniach.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).