Microstructure and hardness of Al2O3-ZrO2-Ti composites
The aim of this work was to fabricate Al2O3-ZrO2-Ti composites by slip casting and to analyse the influence of a pure titanium addition on the microstructure and density of the composites. For this purpose, two groups of samples were prepared by slip casting, with and without titanium. Experiments were performed using the samples: Al2O3 + 10 vol.% ZrO2 and Al2O3 + 10 vol.% ZrO2 + 10 vol.% Ti. The composites were characterized by XRD and SEM. Moreover, the density was measured using the Archimedes method. The hardness was measured as well. The obtained composites had a homogeneous microstructure and high relative density. It was found that a phase transformation in ZrO2 occurred. The titanium content as a ductile phase can slightly reduce the Vickers hardness of the composites.
Celem pracy było wytworzenie kompozytów Al2O3-ZrO2-Ti metodą odlewania z mas lejnych (slip-casting) oraz analiza wpływu dodatku czystego tytanu na mikrostrukturę i gęstość kompozytów. Przygotowano dwa zestawy próbek, różniących się brakiem lub obecnością dodatku tytanu: Al2O3 + 10% obj. ZrO2 oraz Al2O3 + 10% obj. ZrO2 + 10% obj. Ti. Wytworzone kompozyty charakteryzowano za pomocą dyfrakcji rentgenowskiej oraz skaningowej mikroskopii elektronowej. Zagęszczenie kompozytów wyznaczono metodą Archimedesa, natomiast twardość zmierzono metodą Vickersa. W badanych kompozytach otrzymano jednorodną mikrostrukturę oraz wysokie zagęszczenie. Zauważono również obecność przemiany fazowej zachodzącej w dwutlenku cyrkonu. Dodatek fazy plastycznej w postaci tytanu nieznacznie obniżył gęstość oraz twardość badanych kompozytów.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).