Preparation and Morphology of Poly(butylene succinate) Nanofibers via Electrospinning

An electrospinning method was used to produce Poly(butylene succinate) (PBS) nanofibres. The morphology of the fibres was studied considering fibres of different weight concentrations of PBS/CF solution and spun with different diameters of needle-orifice. The results show that the electrospinning process is very difficult and the products are only by few fibres when the weight concentration equals 8%. When the concentration is increased, the eff-iciency is high and the process becomes easy. The morphology of the fibres is more uniform when are spun with a larger diameter of the needle-orifice. The electrospinability ranges between 8 wt% and 14wt% of PBS/CF weight concentration. The thermal properties and the crystallisation of the PBS polymer pellets and electrospun PBS nanofibers were measured by differential scanning calorimetry (DSC) and wide angle X-ray diffraction (WAXD), respectively. In addition, the hydrolytic degradation behaviour of electrospun PBS nanofibres in 1N NaOH solution was observed by using scanning electron microscopy (SEM).

---

Elektroprżedzenie zastosowano do wytworzenia nanowłókien z poli(butyleno bursztynianu) (PBS) z roztworów chlorowormu o różnej zawartości PBS i przędzionych przy użyciu igieł o różnych średnicach. Wyniki pokazują, że proces elektroprzędzenia jest bardzo trudny i można uzyskac włókna z roztworu o stężeniu 8 %wt. Kiedy stężenie wzrasta, wzrasta wydajność i proces przebiega łatwo. Istnieje możliwość elektroprzędzenia przy stężeniach 8 do 14 wt% PBS/CF. Właściwości termiczne i krystalizacja granulek PBS oraz nanowłókien PBS zostały wyznaczone przy użyciu DSC i WAXD. Ponadto, degradacja hydrolityczna nanowłokien PBS w 1N roztworze NaOH była obserwowana przy pomocy SEM.