The tribological properties of sinteres steel-matrix composites
The tribological properties of composite materials reinforced with titanium diboride were investigated. Abrasion resistance tests were carried out at room temperature in a ball-on-disc system. Balls with a diameter of 3.14 mm were used as the counter-samples. The effect of the TiB2 content and counter-sample material (Al2O3, Si3N4, ZrO2, AISI52100 steel) on the coefficient of friction and wear rate of the sintered composites and 316L steel was determined. After the abrasion tests the sample surfaces were examined by scanning electron microscopy. The obtained results show that the tribological properties depend on the test conditions and content of the TiB2 reinforcing phase.
W pracy przedstawiono właściwości tribologiczne materiałów kompozytowych wzmacnianych dwuborkiem tytanu. Badania odporności na zużycie przeprowadzono w temperaturze pokojowej w skojarzeniu kulka-tarcza. Jako przeciwpróbki użyto kulki o średnicy 3,14 mm. Określono wpływ ilości TiB2 i materiału przeciwpróbki (Al2O3, Si3N4, ZrO2, stal AISI52100) na współczynnik tarcia oraz zużycie spiekanych materiałów kompozytowych i stali 316L. Powierzchnie próbek po testach tribologicznych obserwowano za pomocą skaningowego mikroskopu elektronowego. Uzyskane wyniki badań wykazały, że na właściwości tribologiczne wpływają warunki badań i ilość fazy wzmacnianej TiB2.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).