Characteristic of cyclic oxidation of chosen austenitic steels in a steam atmosphere
The aim of the study was to evaluate the oxidation resistance of chromium-nickel austenitic steels in an atmosphere, which contains oxygen and steam at a temperature of 750oC. The oxidation test of steel samples X2CrNiMo17-12-2, X6CrNiMoTi17-12-2, Super 304H and HR3C was carried out in a cyclic mode, made up of 100 cycles trials of 2 hours. The results show the mass changes of steels caused by a cyclic oxidation. The morphology and chemical composition of the oxide layer formed on the surface of tested samples were also described. It has been proved that under these conditions HR3C steel shows the best heat resistance and X2CrNiMo17-12-2 steel presents the worst tendency of oxides to defoliation.
Celem badań była ocena odporności na utlenianie austenitycznych stali chromowo-niklowych w atmosferze zawierającej tlen i parę wodną w temperaturze 750oC. Utlenianie próbek ze stali X2CrNiMo17-12-2, X6CrNiMoTi17-12-2, Super 304H i HR3C przeprowadzono w sposób cykliczny, składający się ze 100 cykli trwających 2 godziny. Przedstawiono wyniki zmiany masy materiałów wywołanych cyklicznym utlenianiem. Scharakteryzowano również morfologię i skład chemiczny warstw tlenkowych powstałych na powierzchni badanych stali. Wykazano, że najlepszą żaroodporność w tych warunkach posiada stal HR3C, a najgorszą stal X2CrNiMo17-12-2 wykazująca skłonność do defoliacji tlenków.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.