Tytuł pozycji:
Influence of alloying elements on the microstructure of new cobalt matrix superalloys reinforced with phase - L12
The article presents selected results of research on the primary structure of a new generation of cobalt-based Co-20Ni-10Al-5Mo-2Nb superalloys. Research on this group of materials was started in 2006 by J. Sato. These materials are anticipated to be able to replace nickel-based superalloys in the future due to their superior elevated temperature properties compared to the nickel-based superalloys. Today, γ’ nickel-based superalloys are still unrivalled in aerospace applications, however, cobalt-based superalloys are a response to their existing limitations, which do not allow the current pace of aircraft engine development to be maintained.
W pracy przedstawiono wybrane wyniki badań nad pierwotną strukturą nowej generacji nadstopów na osnowie kobaltu typu Co-20Ni-10Al-5Mo-2Nb. Badania nad tą grupą materiałów rozpoczął w 2006 roku J. Sato. Przewiduje się, że materiały te w przyszłości mogą zastąpić nadstopy na osnowie niklu ze względu na ich doskonałe właściwości w podwyższonej temperaturze w porównaniu z nadstopami na osnowie niklu. Obecnie nadstopy na osnowie niklu wzmacniane fazą γ’ są nadal bezkonkurencyjne w zastosowaniach lotniczych, jednak nadstopy na bazie kobaltu są odpowiedzią na ich istniejące ograniczenia, które nie pozwalają na utrzymanie obecnego tempa rozwoju silników lotniczych.
Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2020).