Influence of Chemical and Mineralogical Composition of Steelmaking Slags on their Next Utilization
The major waste products of metallurgical production are slags. The amount of steelmaking slag is about 65-150 kg per tonne of crude steel produced. At present, there is an effort to reduce the amount of slag arising, which is possible by pretreatment of pig iron, secondary metallurgy of molten steel and careful selection of batch materials. Despite all efforts, the amount of slag produced represents about 13% of the total batch. The paper focuses exclusively on primary slags from the steelmaking process in the oxygen converter and the electric arc furnace. The chemical and mineralogical composition of the steelmaking slag will be the most significant factor affecting its further potential use. Authors describes hydraulicity of slags as function of composition, and also their next utilization in concrete construction.
Głównymi odpadami metalurgicznymi są żużle. Ilość żużla stalowniczego wynosi około 65-150 kg na tonę wyprodukowanej surowej stali. Obecnie dąży się do zmniejszenia ilości powstających żużli, co jest możliwe dzięki obróbce wstępnej surówki, wtórnej metalurgii stali i starannej selekcji materiałów wsadowych. Pomimo wszystkich zabiegów, ilość wytwarzanego żużla stanowi około 13% całkowitej produkcji. Artykuł koncentruje się głównie na żużlach z procesów stalowniczych z konwertora tlenowego i elektrycznego pieca łukowego. Skład chemiczny i mineralogiczny żużla stalowniczego jest najważniejszym czynnikiem wpływającym na jego dalsze potencjalne wykorzystanie. Autorzy opisują hydrauliczność żużli jako funkcję składu, a także ich kolejne wykorzystanie w konstrukcjach betonowych.
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).