Synthesis of Modified Polyimidoamide Designed for Fibre Spinning

Polyimidoamide prepared from trimellite anhydride and 4,4'-diisocyanatediphenylenemethane was modified by introducing slight quantities of flexible segments such as -C6H4-CH2-C6H4- derived from 4,4'-diaminediphenylenemethane into the polymer chain. The synthesis was performed in two stages. In the first stage, a pre-polymer terminated with carboxylic or anhydride groups was obtained using a slight excess of trimellite anhydride; in the second stage, the diamine mentioned was added which joined the pre-polymer molecules into a long chain. The effects of monomer concentration, molar ratio, time and temperature on the course and results of the synthesis were examined.

---

Poliimidoamidy otrzymane z trójmelitowego bezwodnika i 4,4'-dwuizocjanianufenylenometanu modyfikowano przez wprowadzenie do łańcucha polimerowego małych giętkich segmentów, takich jak -C6H4-CH2-C6H4- otrzymanych z 4,4'-dwuaminodwufenylenometanu. Syntezę przeprowadzono dwustopniowo. W pierwszym etapie otrzymywano prepolimer zakończony grupami karboksylowymi lub bezwodnikowymi przy małym nadmiarze bezwodnika trójmelitowego, w drugim dodawano wspomnianą dwuaminę, która łączyła cząsteczki prepolimeru w długie łańcuchy. Badano wpływ stężenia monomeru, stosunku molowego, czasu i temperatury na przebieg syntezy i otrzymywane produkty.