Direct Determination Of γ′ / γ′+γ / γ Phase Boundaries in Ni-Al-Cr System Based on Enthalpy of Formation Results Obtained by Calorimetric Solution Method

he work is a continuation of the research carried out on a high-temperature calorimeter solution type on alloys from Ni-Al-Cr system. Thanks to the construction innovation introduced by authors the device allows the determination of the formation enthalpy of alloys at ambient and elevated temperatures. Experiments described in this article were carried out at three temperatures: 873K, 996K and 1150K on the alloys of the chemical compositions from the Ni75Al25 ÷ Ni87Cr13 section of the Ni-Al-Cr system. On the basis of changes in the enthalpy of formation with increasing chromium content of the alloys, points corresponding to places of phase boundaries γ′ / γ′+γ / γ in Ni-Al-Cr system were determined. A similar relationship was observed in previous studies of alloys from Ni75Al25÷Ni75Cr25 section. For precise determination of these characteristic points a statistical model was applied.

---

Praca jest kontynuacją badań prowadzonych na skonstruowanym przez autorów wysokotemperaturowym kalorymetrze typu rozpuszczania. Urządzenie pozwala na określanie entalpii tworzenia stopów w podwyższonej temperaturze. Opisywane badania przeprowadzono w trzech temperaturach: 873K, 996K i 1150K na stopach o składach chemicznych znajdujących się na linii Ni75Al25÷Ni87Cr13 układu Ni-Al-Cr. Na podstawie zmian wartości entalpii tworzenia wraz ze wzrostem zawartości chromu w stopach stwierdzono istnienie punktów odpowiadających miejscom występowania granic międzyfazowych γ′ / γ′+γ / γ w układzie Ni-Al-Cr. Podobną zależność zaobserwowano w poprzednich badaniach dotyczących obszaru Ni75Al25÷Ni75Cr25. Aby precyzyjnie wyznaczyć te charakterystyczne punkty opracowano i zastosowano model statystyczny.