Discussion on the Tensile and Bending Properties of PAN-based Pre-oxidised Fibre Felt Composite Materials
The impact of the mass percentage of PAN-based pre-oxidised fibre felt in a composite material and of the curing temperature on the composite material’s mechanical properties were studied in order to optimise the preparation method of epoxy resin composite material. The results showed that when the dosage of PAN-based pre-oxidised fibre felt was 15% of the mass of epoxy resin and the curing temperature was 170 °C, the tensile and bending properties of the composite materials produced were the best. This study has addressed the absence of reports on this type of composite material, and is expected to lead to the development of applications for this new type of composite material.
W celu zoptymalizowania metody przygotowania materiału kompozytowego z żywicy epoksydowej zbadano wpływ procentu masy wstępnie utlenionego filcu z włókien PAN w materiale kompozytowym i temperatury utwardzania na właściwości mechaniczne materiału kompozytowego. Wyniki pokazały, że najlepsze właściwości rozciągania i zginania wytwarzanych materiałów kompozytowych otrzymano dla 15% ilość wstępnie utlenionego filcu z włókien PAN w stosunku do masy żywicy epoksydowej, a optymalna temperatura utwardzania wynosiła 170 °C. Autorzy pracy oczekują, że przeprowadzone badanie doprowadzi w przyszłości do opracowania aplikacji dla nowego rodzaju materiału kompozytowego.
Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2020).