Influence of Hydration on Transport and Storage of Spinel-Based Refractory Raw Materials

This work concerns the hydration resistance of spinel MgAl2O4-based aggregates which comprise the common raw materials for the production of refractories. A sintered product along with the melted one were taken for the investigation. The starting materials were characterized in terms of their chemical and phase composition by XRF and XRD methods, respectively. Subsequently, the samples were subjected to hydration test according to ASTM C 554-92. The after-hydration samples were analyzed by XRD and SEM/EDS methods. It was found that sintered spinel aggregates enriched in Mg2+ ions and containing free MgO are highly susceptible to water exposure.

---

Praca dotyczy badania i oceny odporności na hydratację spiekanych i topionych kruszyw na bazie spinelu MgAl2O4, które stanowią grupę surowców szeroko stosowanych do produkcji formowanych i nieformowanych materiałów ogniotrwałych. Wyjściowe materiały zbadano pod względem ich składu fazowego (XRD) i chemicznego (XRF). Następnie przeprowadzono badanie hydratacji metodą autoklawizacji według normy ASTM C 554-92. Próbki po hydratacji poddano analizie składu fazowego (XRD) i mikrostruktury (SEM/EDS). Badania wykazały, iż kruszywa spinelowe wzbogacone w spinel o nadmiarze jonów Mg2+ i zawierające wolny MgO wykazują największą zdolność do hydratacji.