Hydrogen Sensor Of TiO2-Based Nanomaterials
The aim of this research was to examine gas sensing properties of TiO2 based nanomaterials. Nanopowders of Cr doped TiO2 with constant Specific Surface Area, SSA, were obtained using Flame Spray Synthesis technique, FSS. Nanomaterials were characterized by Brunauer – Emmett – Teller adsorption isotherms, BET, X – ray diffraction, XRD, Transmission Electron Microscopy, TEM, optical spectrometry UV – vis with the use of an integrating sphere as well as impedance spectroscopy. Detection of hydrogen was carried out over the concentration range of 50 - 3000 ppm at the temperatures extending from 200 to 400°C and synthetic air working as a reference atmosphere. As a result of experiments it appeared that incorporation of 5 at.% of Cr into TiO2 improved hydrogen sensing features due to small crystallite size and predominance of rutile polymorphic phase.
Przedmiotem pracy są nanomateriały na bazie TiO2 do zastosowań sensorowych. Nanoproszki TiO2 domieszkowane chromem o stałej powierzchni właściwej SSA (ang. Specific Surface Area) otrzymano przy pomocy techniki syntezy w płomieniu FSS (ang. Flame Spray Synthesis). Materiały poddano charakteryzacji z wykorzystaniem: izoterm adsorpcyjnych Brunauer – Emmett – Teller, BET, dyfraktometrii rentgenowskiej, XRD, transmisyjnej mikroskopii elektronowej, TEM, spektroskopii optycznej UV – vis oraz spektroskopii impedancyjnej. Pomiar własności sensorowych został przeprowadzony dla koncentracji H2 w zakresie 50-3000 ppm w przedziale temperatur 200-400°C. Wykazano, że najlepiej na wodór odpowiada próbka TiO2: 5 at.% Cr charakteryzująca się małym rozmiarem krystalitów oraz przewagą fazy rutylu.
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.