Wear testing of α-Al2O3 oxide ceramic in a diverse abrasive soil mass

This paper presents a comparative study of the intensity of α-Al2O3 oxide ceramic sand 38GSA martensitic steel wear in three types of abrasive soil masses, i.e. loose sand, sandy clay and heavy clay. The tests were carried out under laboratory conditions on a "spinning bowl" wear machine. Based on the obtained results, the intensity of ceramic material wear was many times lower than 38GSA steel wear. It was found that the granulometric composition had an important effect on the intensity of α-Al2O3 ceramics wear. The lowest α-Al2O3 oxide ceramics wear was obtained during friction in sandy clay, and it was 1.5 times lower than in heavy clay and 1.9 times lower than in loose sand. Differences in the types of tribological wear, depending on the granulometric abrasive mass composition, are described.

---

W pracy przedstawiono badania porównawcze intensywności zużywania ceramiki tlenkowej α-Al2O3 i martenzytycznej stali 38GSA w trzech rodzajach glebowych mas ściernych tj. piasku luźnym, glinie piaszczystej i glinie ciężkiej. Badania przeprowadzono w warunkach laboratoryjnych na maszynie zużyciowej „wirującej misy". Na podstawie uzyskanych wyników stwierdzono, że intensywność zużywania materiału ceramicznego była wielokrotnie mniejsza od zużycia stali 38GSA. Stwierdzono, że skład granulo-metryczny ma istotny wpływ na intensywność zużywania ceramiki α-Al2O3. Najmniejsze zużycie ceramiki tlenkowej α-Al2O3 uzyskano podczas tarcia w glinie piaszczystej i było ono 1,5-krotnie mniejsze niż w glinie ciężkiej i 1,9-krotnie mniejsze niż w piasku luźnym. Opisano różnice w sposobach zużywania tribologicznego w zależności od składu granulometrycznego masy ściernej.