The effect of the TIG method-based melting of welds on the properties and the structure of welded joints made of austenitic steel
The article discusses the effect of TIG method-based melting on the properties and the structure of welded joints made of austenitic steel AISI 304. The tests involved the making of 2 mm thick joints and their subsequent melting in two different ways, i.e. with maintaining interpass temperature and immediately after welding. The study also included the performance of mechanical tests, macro and microscopic metallographic tests as well as hardness and corrosion resistance tests. Results obtained in the tests justified the conclusion that the melting process and its conditions significantly affect the properties and the structure of welded joints.
W niniejszym artykule zbadano wpływ przetapiania spoiny metodą TIG na własności oraz strukturę złączy spawanych stali austenitycznej X5CrNi18-10. W tym celu wykonano złącza próbne blach o grubości 2 mm, a następnie poddano je przetopieniu na dwa różne sposoby, tj. z zachowaniem temperatury międzyściegowej oraz bezpośrednio po spawaniu. Następnie przeprowadzono badania wytrzymałościowe, metalograficzne makro- i mikroskopowe, pomiary twardości oraz badania odporności korozyjnej. Na ich podstawie oceniono, że przetopienie oraz jego warunki w znacznym stopniu wpływają na własności i strukturę złącza spawanego.
Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).