Electron beam surface hardening of gear teeth
Surface hardening is an effective method enabling the improvement of the wear resistance of components subjected to friction, without the necessity of hardening the entire component. Because of easy dynamic deflection and focusing as well as due to very high heating rates, the use of electron beam enables the obtainment of layers characterised by suitable properties. The article describes the electron beam surface hardening of gear teeth made of steel 34CrAlNi7-10 (1.8550) as well as discusses metallographic test results and Vickers hardness measurement results demonstrating the effectiveness of the method in the obtainment of layers characterised by uniform thickness and a hardness of 660 HV0.1.
Hartowanie powierzchniowe jest skuteczną metodą poprawy odporności na zużycie elementów narażonych na tarcie, bez konieczności hartowania całego elementu. Zastosowanie wiązki elektronów umożliwia uzyskanie warstw o odpowiednich właściwościach, dzięki łatwemu, dynamicznemu odchylaniu i ogniskowaniu oraz bardzo wysokim szybkościom nagrzewania. W artykule przeprowadzono proces hartowania powierzchniowego uzębień kół zębatych ze stali 34CrAlNi7-10 (1.8550) za pomocą wiązki elektronów. Przeprowadzono badania metalograficzne i pomiar twardości metodą Vickersa, dzięki którym przedstawiono skuteczność tej metody, uzyskując warstwy o równomiernej grubości i twardości rzędu 660 HV0,1.
Opracowanie rekordu ze środków MNiSW, umowa nr POPUL/SP/0154/2024/02 w ramach programu "Społeczna odpowiedzialność nauki II" - moduł: Popularyzacja nauki (2025).